A popular choice for the placement of fixed restorations, dental resin cements are available in a range of compositions with different curing options, application protocols, working times and other physical properties. Often formulated from blends of methacrylates, dimethacrylates, and polymethacrylates, resin cements are designed to provide high strength bonds that withstand the rigors of the intraoral environment. Often resin cements work best with proper etching protocols, and in the case of some resin cements, a bonding agent. It is important to follow the manufacturer’s application protocol and use the cement with appropriate complementary materials.
|  |  |
| Company | Premier Dental Products Company | Premier Dental Products Company |
| Item | NexTemp Temporary Resin Cement | ZR-Cem Self-Adhesive Universal Resin Cement |
| Price | Inquire | Inquire |
| Description | NexTemp temporary resin cement from Premier is designed to combine the multiple benefits of fluoride release, potassium nitrate, and Chlorhexidine. | This self-adhesive universal resin cement is specially formulated for zirconia restorations. The BPO/amine-free initiation system leads to exceptional |
| Cure Type | Not Available | Dual-cure |
| Fluoride Release | Yes | Not Available |
| Shades Available | Not Available | Opaque White, Shade A2 and Translucent |
| Compressive Strength | 2,901 psi (20 MPa) | 150 MPA |
| Film Thickness | Not Available | 10 um |
| Working Time | Not Available | 1.5 - 2.5 minutes. |
| Set Time | Not Available | 3.0 - 4.0 minutes. |
| Radiopaque | No | 250% Al |
| Bond Strength | Not Available | The cement’s formula contains 10-MDP to enable a strong bond to all-ceramic materials, dentin and enamel for optimal retention and marginal integrity. |
| Self Etch | No | Not Available |
| Flexural Strength | Not Available | 100 MPA |
| Try-In Paste | No | Not Available |
| Indicated for Veneers | No | Not Available |
| Contents | 1 Automix Dual-Barrel Syringe (5 mL)
10 Mix Tips | Not Available |
| Get Info | Inquire | Inquire |